Metallocene Plastomer PE KN Grades Line-Up

1. Film grades

Properties Units Test Methods KF260T KF270 KF360T
Typical Applications <Brown
film>		 <Brown
film>		 <Cast film>
<Sealant> <Sealant> <Sealant>
<Stretch film> <Stretch film> <Stretch film>
<Bag in Box> <Bag in Box> 　
Polymer Properties Melt
Flow Rate M F R		 g/10min JIS K6922-2 2 2 3.5
Density g/㎤ JIS K6922-1,2 0.901 0.907 0.898
Tensile Yield ㎫ JIS K6922-2 n.d n.d n.d
Elongation at
Break		 % JIS K6922-2 >500 >500 >500
Flexural
Modulus		 ㎫ JIS K6922-2 82 114 56
Chirpy Impact
Strength		 kJ/㎡ JIS K6922-2 No Break No Break No Break
Hardness HDD JIS K7215 44 47 42
ESCR h ASTM D1693 >1000 >1000 >1000
Vicat
Softening Point		 ℃ JIS K7206 80 88 72
DSC melting
Point		 ℃ ISO 11357-3 93 100 90
Brittle Point ℃ ISO FDIS974 <-70 <-70 <-70
Test Piece 　 JISK6922-2 Compression Molding
Key Points <Super low
temperature>
<Heatsealability>		 <Super low
temperature>
<Heatsealability>		 <Super low
temperature>
<Heatsealability>

2. Extrusion coating grades

Properties Units Test Methods KC570S
Typical Applications <Sealant>
<Higher Packing Speed>
Polymer Properties Melt
Flow Rate M F R		 g/10min JIS K6922-2 10.5
Density g/㎤ JIS K6922-1,2 0.906
Tensile Yield ㎫ JIS K6922-2 n.d
Elongation at
Break		 % JIS K6922-2 >500
Flexural
Modulus		 ㎫ JIS K6922-2 108
Chirpy Impact
Strength		 kJ/㎡ JIS K6922-2 No Break
Hardness HDD JIS K7215 42
ESCR h ASTM D1693 <1000
Vicat
Softening Point		 ℃ JIS K7206 73
DSC melting
Point		 ℃ ISO 11357-3 102
Brittle Point ℃ ISO FDIS974 <-70
Test Piece 　 JISK6922-2 Compression Molding
Key Points <Low
temperature>
<Heatsealability>
<Low neck in>

3. Injection, Modifier Grades

Properties Units Test Methods KS340T KS560T KJ640
Typical Applications <Sheet>
<Stationary>
<Industrial parts>
<Commodity>		 <Sheet>
<Stationary>
<Industrial parts>
<Commodity>		 <Sheet>
<Stationary>
<Industrial parts>
<Commodity>
Polymer Properties Melt
Flow Rate M F R		 g/10min JIS K6922-2 3.5 16.5 30
Density g/㎤ JIS K6922-1,2 0.880 0.898 0.880
Tensile Yield ㎫ JIS K6922-2 n.d n.d n.d
Elongation at
Break		 % JIS K6922-2 >500 >500 >500
Flexural
Modulus		 ㎫ JIS K6922-2 23 62 23
Chirpy Impact
Strength		 kJ/㎡ JIS K6922-2 No Break No Break No Break
Hardness HDD JIS K7215 30 40 27
ESCR h ASTM D1693 >1000 >1000 >1000
Vicat
Softening Point		 ℃ JIS K7206 44 66 39
DSC melting
Point		 ℃ ISO 11357-3 60 90 58
Brittle Point ℃ ISO FDIS974 <-70 <-70 <-70
Test Piece 　 JISK6922-2 Compression Molding
Key Points <Injection>
<Modifier>
<Softness>		 <Injection>
<Modifier>
<Softness>		 <Injection>
<Modifier>
<Softness>
We do not guarantee the typical values.